| Peer-Reviewed

Metal Nanowires Subjected to Relavant Hydrated Metal Ions

Received: 9 February 2017     Published: 10 February 2017
Views:       Downloads:
Abstract

The hcp-Co and fcc-Ni nanowires with the diameter of ~ 50nm were successfully prepared at different overpotentials by using potentiostatic electrochemical deposition in the pores of AAO templates. The prepared nanowires were characterized by X-ray diffraction, and the morphology of the nanowires was investigated by scanning electron microscope. In this study a new way is established to understand the growth rate of nanowires. The effect of work function on the growth rate of Co and Ni nanowires having same electrolyte’s concentration, same pH value, and same overpotentials, has been discussed. The growth rate of metal nanowires in ECD is determined by the tunneling current between a metal and hydrated metal ions. The higher the tunneling current, the higher will be the growth rate. The tunneling current probably relates to the work function of metal. The larger is the value of work function the lower is the probability of electron tunneling. Lowering the work function causes increase in the current density. The hydrated Co and Ni ions are of octahedral structure with M-O distance of 2.08 Å and 2.05 Å, respectively. The work function of Co is smaller, this lead to higher tunneling current density. Therefore, the measured current density is higher for Co than for Ni and the Co nanowires grow faster than that of the Ni nanowires.

Published in International Journal of Materials Science and Applications (Volume 6, Issue 2)
DOI 10.11648/j.ijmsa.20170602.14
Page(s) 88-94
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2017. Published by Science Publishing Group

Keywords

Crystal Structure, Nucleation, Growth from Solutions, Deposition Parameters

References
[1] Gudiksen, M. S., et al., Growth of nanowire superlattice structures for nanoscale photonics and electronics. Nature, 2002. 415 (6872): p. 617-620.
[2] Sun, S., et al., Monodisperse FePt Nanoparticles and Ferromagnetic FePt Nanocrystal Superlattices. Science, 2000. 287 (5460): p. 1989-1992.
[3] Kim, S.-W., et al., Fabrication of Hollow Palladium Spheres and Their Successful Application to the Recyclable Heterogeneous Catalyst for Suzuki Coupling Reactions. Journal of the American Chemical Society, 2002. 124 (26): p. 7642-7643.
[4] Lee, S. B., et al., Antibody-Based Bio-Nanotube Membranes for Enantiomeric Drug Separations. Science, 2002. 296 (5576): p. 2198-2200.
[5] Martin, C. R., Nanomaterials: A Membrane-Based Synthetic Approach. Science, 1994. 266 (5193): p. 1961-1966.
[6] Whitney, T. M., et al., Fabrication and Magnetic Properties of Arrays of Metallic Nanowires. Science, 1993. 261 (5126): p. 1316-1319.
[7] Wen-Ching Tsai, C.-C. W., and Yung-Yun Wang, Frequency Effect of Pulse Plating on the Uniformity of Copper Deposition in Plated Through Holes. J. Electrochem. Soc., 2003. 150 (5): p. 267-272.
[8] A. J. Yin, J. L., W. Jian, A. J. Bennett, and J. M. Xu, Fabrication of highly ordered metallic nanowire arrays by electrodeposition. Applied Physics Letters, 2001. 79 (7): p. 1039.
[9] El‐Giar, E. M., et al., Localized Electrochemical Deposition of Copper Microstructures. Journal of The Electrochemical Society, 2000. 147 (2): p. 586-591.
[10] Routkevitch, D., et al., Electrochemical Fabrication of CdS Nanowire Arrays in Porous Anodic Aluminum Oxide Templates. The Journal of Physical Chemistry, 1996. 100 (33): p. 14037-14047.
[11] Kim, F. S., J. H. & Yang, P. D, Photochemical synthesis of gold nanorods. Journal of American Chemical Society, 2002. 124 (48): p. 14316-14317.
[12] Huang, Y.D., X.F.; Cui, Y. & Lieber, C. M, Gallium Nitride Nanowire Nanodevices. Nano Lettres, 2002. 2 (2): p. 101-104.
[13] Björk, M. T. O., B. J.; Sass, T.; Persson, A. I.; Thelander, C.; Magnusson M. H.; Deppert, K.; Wallenberg, L. R. & Samuelson, L., One-dimensional Steeplechase for Electrons Realized. Nano Letters, 2002. 2 (2): p. 87 – 89.
[14] Wei Wu, B. C., Xiao-yun Sun, Wei Zhang, Lei Zhuang, Linshu Kong, and Stephen Y. Chou, Large area high density quantized magnetic disks fabricated using nanoimprint lithography. J. Vac. Sci. Technol. B, 1998. 16 (6): p. 3825-9.
[15] Gary M. McClelland, M. W. H., Charles T. Rettner, Margaret E. Best, Kenneth R. Carter, and Bruce D. Terris, Nanoscale patterning of magnetic islands by imprint lithography using a flexible mold. Appl. Phys. Lett., 2002. 81 (8): p. 1483-5.
[16] Whitney, T. M., et al., Fabrication and magnetic properties of arrays of metallic nanowires. Science (New York, N. Y.), 1993. 261 (5126): p. 1316-1319.
[17] J. M. García, A. A., J. Velázquez1, D. García, M. Vázquez, P. Aranda, and E. Ruiz-Hitzky, Magnetic behavior of an array of cobalt nanowires. J. Appl. Phys., 1999. 85 (8): p. 5480-2.
[18] D. J. Sellmyer, M. Z., R. Skomski, Magnetism of Fe, Co, and Ni Nanowires in Self-Assembled Arrays. J. Phys. Condens. Matter, 2001. 13: p. R433-R460.
[19] Skomski R, K. R. D. a. S. D. J., J. Appl. Phys., 1999. 85: p. 5069–71.
[20] Han G C, Zong B Y, and W. Y. H, IEEE Trans. Magn, 2002: p. 2562–4.
[21] Inguanta, R., S. Piazza, and C. Sunseri, Influence of the electrical parameters on the fabrication of copper nanowires into anodic alumina templates. Applied Surface Science, 2009. 255 (21): p. 8816-8823.
[22] Yu, Y. Y. C., S. S.; Lee, C. L. & Wang, C. R. C., Gold Nanorods: Electrochemical Synthesis and Optical Properties. Journal of Physical Chemistry B, 1997. 101 (34): p. 6661-6664.
[23] Xu, J. and K. Wang, Pulsed electrodeposition of monocrystalline Ni nanowire array and its magnetic properties. Applied Surface Science, 2008. 254 (20): p. 6623-6627.
[24] Ozin, G. A., Nanochemistry: Synthesis in diminishing dimensions. Advanced Materials, 1992. 4 (10): p. 612-649.
[25] Tonucci, R. J., Justus, B. J., Campillo, A. J., and Ford, C. E, NANOCHANNEL ARRAY GLASS. Science, 1992. 258 (5083): p. 783-785.
[26] K. Nielsch, R. B. W., J. Barthel, J. Kirschner, U. Gosele, S. F. Ficher, H. Kronmuller, Hexagonally ordered 100 nm period nickel nanowire arrays. Appl. Phys. Lett., 2001. 79 (9): p. 1360 -2.
[27] Fashen Li, T. W., Liyuan Ren and Jianrong Sun, Structure and magnetic properties of Co nanowires in self-assembled arrays. J. Phys.: Condens. Matter 2004. 16 (45): p. 8053.
[28] M. Darques, A. E., L. Vila, L. Piraux, Controlled changes in the microstructure and magnetic anisotropy in arrays of electrodeposited Co nanowires induced by the solution pH. J. Phys. D: Appl. Phys., 2004. 37 (10): p. 1411.
[29] M. Darques, L. P., A. Encinas, P. Bayle-Guillemaud, A. Popa, U. Ebels,, Electrochemical control and selection of the structural and magnetic properties of cobalt nanowires. Appl. Phys. Lett., 2005. 86 (7): p. 072508-72510.
[30] Wang XW, F. G., Xu XJ, Jin Z, Zhang LD, Size-dependent orientation growth of large-area ordered Ni nanowire arrays. J Phys Chem B., 2005. 109 (51): p. 24326-30.
[31] Xue Wei Wang, G. T. F., Li Chen, Xi Jin Xu and Li De Zhang, Orientation-Controllable Growth of Ni Nanowire Arrays with Different Diameters. Electrochem. Solid-State Lett., 2007. 10 (4): p. E1-E3.
[32] Huang, et al., Orientation-Controlled Synthesis and Ferromagnetism of Single Crystalline Co Nanowire Arrays. The Journal of Physical Chemistry C, 2008. 112 (5): p. 1468-1472.
[33] Mukhtar, A., et al., Effect of Co2+ concentration on the crystal structure of electrodeposited Co nanowires. Journal of Crystal Growth, 2016. 441: p. 26-32.
[34] Mehmood, T., et al., Mechanism for formation of fcc-cobalt nanowires in electrodeposition at ambient temperature. Materials Letters, 2014. 130 (0): p. 256-258.
[35] Mehmood, T., et al., Influence of bath temperature and pH on the structure of electrodeposited cobalt nanowires. International Journal of Materials Research, 2015. 106 (9): p. 957-961.
[36] Mehmood, T., et al., Growth Mechanism of Electrodeposited Fe, Co and Ni Nanowires in the Form of Self-Assembled Arrays at Fixed Potential. Int. J. Electrochem. Sci, 2016. 11: p. 6423-6431.
[37] Biao Wang, G. T. F., Min Wang, Ming Guang Kong and Li De Zhang, Preparation of photonic crystals made of air pores in anodic alumina. Nanotechnology, 2007. 18 (36): p. 365601-4.
[38] Masuda, H. and K. Fukuda, Ordered Metal Nanohole Arrays Made by a Two-Step Replication of Honeycomb Structures of Anodic Alumina. Science, 1995. 268 (5216): p. 1466-1468.
[39] Levine, I. N., Physical Chemistry. McGraw-Hill Book Company, New York, 1978: p. 350-396.
[40] Jonghe, J. W. E. a. L. C. D., The Production of Inorganic Materials. Macmillan Publishing Company, New York, 1991: p. 1497-149.
[41] M. Paunovic and M. Schlesinger., Fundamentals of Electrochemical Deposition. 1998, New York: Wiley.
[42] Persson, I., Hydrated metal ions in aqueous solution: How regular are their structures? Pure and Applied Chemistry, 2010. 82 (10): p. 1901.
[43] Tsong, T. T., Atom-probe field ion microscopy. 1990, Cambridge, New York: Cambridge University Press.
[44] Gomer, R., Field Emission and Field Ionisation Havard University, Cambridge, 1961.
[45] Paunovic, M. and M. Schlesinger, Fundamentals of Electrochemical Deposition.. 1998, New York: Wiley.
[46] Lower, S. K., Electrochemistry. Textbook: Simon Fraser University.
[47] Pearson, R. G., Hard and Soft Acids and Bases. Journal of the American Chemical Society, 1963. 85 (22): p. 3533-3539.
[48] Beattie, J. K., et al., Structural studies on the caesium alums, CsM [SO4] 2 [middle dot] 12H2O. Journal of the Chemical Society, Dalton Transactions, 1981. 0 (10): p. 2105-2111.
[49] Ohtaki, H. and T. Radnai, Structure and dynamics of hydrated ions. Chemical Reviews, 1993. 93 (3): p. 1157-1204.
[50] Johansson, G., Structures of Complexes in Solution Derived from X-Ray Diffraction Measurements, in Advances in Inorganic Chemistry, A. G. Sykes, Editor. 1992, Academic Press. p. 159-232.
[51] Kristiansson, O., et al., A structural study of the hydrated and the dimethylsulfoxide, N, N'-dimethylpropyleneurea, acetonitrile, pyridine and N, N-dimethylthioformamide solvated nickel (II) ion in solution and solid state. Inorganica Chimica Acta, 2003. 344: p. 15-27.
[52] Eastman, D. E., Photoelectric Work Functions of Transition, Rare-Earth, and Noble Metals. Physical Review B, 1970. 2 (1): p. 1-2.
[53] Trigg, L., Encyclopedia of Physics (second edition). New York, 1991: p. 1308.
Cite This Article
  • APA Style

    Aiman Mukhtar, Tahir Mehmood. (2017). Metal Nanowires Subjected to Relavant Hydrated Metal Ions. International Journal of Materials Science and Applications, 6(2), 88-94. https://doi.org/10.11648/j.ijmsa.20170602.14

    Copy | Download

    ACS Style

    Aiman Mukhtar; Tahir Mehmood. Metal Nanowires Subjected to Relavant Hydrated Metal Ions. Int. J. Mater. Sci. Appl. 2017, 6(2), 88-94. doi: 10.11648/j.ijmsa.20170602.14

    Copy | Download

    AMA Style

    Aiman Mukhtar, Tahir Mehmood. Metal Nanowires Subjected to Relavant Hydrated Metal Ions. Int J Mater Sci Appl. 2017;6(2):88-94. doi: 10.11648/j.ijmsa.20170602.14

    Copy | Download

  • @article{10.11648/j.ijmsa.20170602.14,
      author = {Aiman Mukhtar and Tahir Mehmood},
      title = {Metal Nanowires Subjected to Relavant Hydrated Metal Ions},
      journal = {International Journal of Materials Science and Applications},
      volume = {6},
      number = {2},
      pages = {88-94},
      doi = {10.11648/j.ijmsa.20170602.14},
      url = {https://doi.org/10.11648/j.ijmsa.20170602.14},
      eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ijmsa.20170602.14},
      abstract = {The hcp-Co and fcc-Ni nanowires with the diameter of ~ 50nm were successfully prepared at different overpotentials by using potentiostatic electrochemical deposition in the pores of AAO templates. The prepared nanowires were characterized by X-ray diffraction, and the morphology of the nanowires was investigated by scanning electron microscope. In this study a new way is established to understand the growth rate of nanowires. The effect of work function on the growth rate of Co and Ni nanowires having same electrolyte’s concentration, same pH value, and same overpotentials, has been discussed. The growth rate of metal nanowires in ECD is determined by the tunneling current between a metal and hydrated metal ions. The higher the tunneling current, the higher will be the growth rate. The tunneling current probably relates to the work function of metal. The larger is the value of work function the lower is the probability of electron tunneling. Lowering the work function causes increase in the current density. The hydrated Co and Ni ions are of octahedral structure with M-O distance of 2.08 Å and 2.05 Å, respectively. The work function of Co is smaller, this lead to higher tunneling current density. Therefore, the measured current density is higher for Co than for Ni and the Co nanowires grow faster than that of the Ni nanowires.},
     year = {2017}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - Metal Nanowires Subjected to Relavant Hydrated Metal Ions
    AU  - Aiman Mukhtar
    AU  - Tahir Mehmood
    Y1  - 2017/02/10
    PY  - 2017
    N1  - https://doi.org/10.11648/j.ijmsa.20170602.14
    DO  - 10.11648/j.ijmsa.20170602.14
    T2  - International Journal of Materials Science and Applications
    JF  - International Journal of Materials Science and Applications
    JO  - International Journal of Materials Science and Applications
    SP  - 88
    EP  - 94
    PB  - Science Publishing Group
    SN  - 2327-2643
    UR  - https://doi.org/10.11648/j.ijmsa.20170602.14
    AB  - The hcp-Co and fcc-Ni nanowires with the diameter of ~ 50nm were successfully prepared at different overpotentials by using potentiostatic electrochemical deposition in the pores of AAO templates. The prepared nanowires were characterized by X-ray diffraction, and the morphology of the nanowires was investigated by scanning electron microscope. In this study a new way is established to understand the growth rate of nanowires. The effect of work function on the growth rate of Co and Ni nanowires having same electrolyte’s concentration, same pH value, and same overpotentials, has been discussed. The growth rate of metal nanowires in ECD is determined by the tunneling current between a metal and hydrated metal ions. The higher the tunneling current, the higher will be the growth rate. The tunneling current probably relates to the work function of metal. The larger is the value of work function the lower is the probability of electron tunneling. Lowering the work function causes increase in the current density. The hydrated Co and Ni ions are of octahedral structure with M-O distance of 2.08 Å and 2.05 Å, respectively. The work function of Co is smaller, this lead to higher tunneling current density. Therefore, the measured current density is higher for Co than for Ni and the Co nanowires grow faster than that of the Ni nanowires.
    VL  - 6
    IS  - 2
    ER  - 

    Copy | Download

Author Information
  • The State Key Laboratory of Refractories and Metallurgy, Hubei Collaborative Innovation Center for Advanced Steels, International Research Institute for Steel Technology, Wuhan University of Science and Technology, Wuhan, P. R. China

  • The State Key Laboratory of Refractories and Metallurgy, Hubei Collaborative Innovation Center for Advanced Steels, International Research Institute for Steel Technology, Wuhan University of Science and Technology, Wuhan, P. R. China

  • Sections