Scrutiny of Leakage Currents with Insulating Materials for Transistor Applications

Received: 31 July 2018     Accepted: 27 August 2018     Published: 28 September 2018
Views:       Downloads:
Abstract

Continuous reducing the size of transistor technology has enabled extraordinary improvements in the switching speed, density, functionality and cost of microprocessors. Integrated Circuit industry is pursuing Moore’s curve down to deep-nanoscale dimensions. Advanced transistor technology now faces many challenges that together result in static power consumption due to leakage currents. In fact, leakage currents are responsible for more than 50% of the total power consumption in nanoscale designs. In deep-nanoscale arena, this percentage will increase further. However, diagnosing of the interface quality and interaction between insulators and semiconductors is significant to reduce the leakage current and achieve the high performance of switching devices in the nanoscale domain. Continuous scaling down has required drastic decreases of the SiO2 dielectric film thickness to achieve ever-higher capacitance densities. Fundamental limits of SiO2 as a dielectric material, imposed by electron tunneling, will be reached as this SiO2 film thickness approaches ~1nm. Therefore, alternate high-k interlayer dielectric material will be needed to replace SiO2 as a capacitor and gate dielectric material. Numerous alternate high-k materials are being actively investigated, ranging from Al2O3 (k ~ 9) to HfO2 (k ~ 25). High-k materials hold the promise of achieving very high capacitance densities with relatively thick films.

Published in International Journal of Materials Science and Applications (Volume 7, Issue 5)
DOI 10.11648/j.ijmsa.20180705.11
Page(s) 167-173
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2018. Published by Science Publishing Group

Keywords

Dielectric Materials, High-k Materials, Hafnium Oxide, MOS Transistor, Nanoscale Domain

References
[1] G. D. Wilk, R. M. Wallace, and J. M. Anthony, “High-k gate dielectrics: current status and materials properties considerations,” J. Appl. Phys., vol. 89, pp. 5243–5275, 2001.
[2] H. S. Nalwa, Handbook of Low and High Dielectric Constant Materials and Their Applications, Volume 1: Materials and Processing. Academic Press, San Diego, CA. 1999.
[3] R. Singh and R. K. Ulrich, “High and low dielectric constant materials,” Electrochemical Society Interface, vol. 8, pp. 26–30, 1999.
[4] M. Ritala, and M. Leskela, “Atomic layer deposition. In Handbook of Thin Film Materials,” Academic Press, San Diego, CA, vol. 1, pp. 103, 2001.
[5] A. Rahtu, M. Ritala and M. Leskela, “Atomic layer deposition of zirconium titanium oxide from titanium isopropoxide and zirconium chloride,” Chem. Mater., vol. 13, pp. 1528–1532, 2001.
[6] P. Singer, “Intel, IBM commit to high-k, metal gates,” Semiconductor International, 2007.
[7] S. Ogura, P.J. Tsang, W. W. Walker, D. L. Critchlow and J. F. Shepard, “Design and characteristics of the lightly doped drain-source (LDD) insulated gate field effect transistor,” IEEE Transactions on Electron Device, vol. 27, no. 8, pp. 1359-1367, 1980.
[8] H. J. Choi, J. G. Lee and Y. W. Kim, “High Temperature Strength and Oxidation Behavior of Hot-Pressed Silicon Nitride-Disilicate Ceramics,” Journal of Materials Science, vol. 32, no. 7, pp. 1937-1942, 1997.
[9] Y. S. Zheng, K. M. Knowles, J. M. Vieira, A. B. Lopes and F. J. Oliveira, “Microstructure, Toughness and Flexural Strength of Self-Reinforced Silicon Nitride Ceramics Doped with Yttrium Oxide and Ytterbium Oxide,” Journal of Microscopy, vol. 201, no. 2, pp. 238-249, 2001.
[10] I. Khan and M Zulfequar, “Effect of Tellurium on Electrical and Structural Properties of Sintered Silicon Nitride Ceramics,” Physica B, Vol. 404, No. 16, pp. 2395- 3400, 2009.
[11] Y. Zhang, Y. B. Cheng S. Lathabai and K. Hirao, “Erosion Response of Highly Anisotropic Silicon Nitride,” Journal of the American Ceramic Society, Vol. 88, No. 1, pp. 114-120, 2005.
[12] A. Vuckovic, S. Boskovic and L. Zivkovic, “Synthesis of ‘in-Situ’ Reinforced Silicon Nitride Composites,” Journal of the Serbian Chemical Society, Vol. 69, No. 1, pp. 59-67, 2004.
[13] E.H. Kisi and C.J. Howard, “Crystal structure of zirconia phases and interrelation,” Key. Eng. Mater., vol. 153, pp. 1–36, 1998.
[14] J.P. Chang, Y.S. Lin, S. Berger, A. Kepten, R. Bloom, and S. Levy, “Ultrathin zirconium oxide films as alternative gate dielectric,” J. Vac. Sci. Technol., vol. 19, no. 6, pp. 2212 , 2001.
[15] X. Zhao, D. Ceresoli, and D. Vanderbilt, “Structural, electronic, and dielectric properties of amorphous ZrO2 ab initio molecular dynamics,” Phys. Rev., B-71, 085107, 2005.
[16] M.V. Fischetti, “Long range Coulomb interactions in small Si-devices. Part II. Effective electron mobility in thin-oxide structures,” J. Appl. Phys., vol. 89, no. 2, pp. 1232-1250, 2001.
[17] B.H. Lee, L. Kang, W. J. Qi, R. Nieh, Y. Jeon, K. Onishi, J. C. Lee, “Ultrathin hafnium oxide with low leakage and excellent reliability for alternative gate dielectric applications,” IEEE IEDM Technical Digest, Washington, DC, USA, pp. 133-136, 5-8 December 1999.
[18] A. Kingon, J. Maria, and S. Streiffer, “Alternative dielectrics to silicon dioxide for memory and logic devices,” Nature, vol. 406, pp.1032–1038, 2000.
[19] A. Agarwal et al., “Leakage power analysis and reduction: Models, Estimation and Tools,” Proceedings of the IEEE, vol. 152, no. 3, pp. 353-368, May 2005.
[20] B. J. Sheu et al., “BSIM: Berkeley Short-Channel IGFET Model for MOS Transistors,” IEEE Journal of Solid State Circuits, New York, vol.SC-22, no.4, pp. 558-566, Aug. 1987.
[21] K. Roy et al., “Leakage Current Mechanisms and Leakage Reduction Techniques in Deep-Submicrometer CMOS Circuits,” Proceedings of IEEE, New York, vol.91, no.2, pp. 305-327, Feb 2003.
[22] S. Mukhopadhyay et al. “Accurate Estimation of Total Leakage in Nanometer-Scale Bulk CMOS Circuits Based on Device Geometry and Doping Profile,” IEEE Trans. On CAD of IC and Systems, New York, vol.24, no.3, pp. 363-381, March 2005.
[23] Manorama, P. Shrivastava, and S. Akashe, “Design and analysis of leakage current and delay for Double gate MOSFET at 45nm in CMOS technology,” IEEE 7th International Conference on Intelligent Systems and Control (ISCO), Coimbatore, India, 4-5 January 2013.
[24] P. Dwivedi, K. Kumar and A. Islam, “Comparative study of subthreshold leakage in CNFET & MOSFET @ 32-nm technology node,” IEEE International Conference on Microelectronics, Computing and Communications (MicroCom), Durgapur, India, 23-25 January 2016.
[25] H. Ayano, K. Murakami, Y. Matsui, “A novel technique for reducing leakage current by application of zero-sequence voltage,” International Power Electronics Conference (IPEC-Hiroshima 2014 - ECCE ASIA), Hiroshima, Japan, 18-21 May 2014.
[26] P. Verma A. K. Sharma, V. S. Pandey A. Noor and A. Tanwar, “Estimation of leakage power and delay in CMOS circuits using parametric variation,” Perspectives in Science, Elsevier, vol. 8, pp. 760-763, September 2016.
[27] B. V. Subramanyam and S. S. Basha, “Design of low leakage power SRAM using multithreshold technique,” IEEE 10th International Conference on Intelligent Systems and Control (ISCO), Coimbatore, India, 7-8 January 2016.
[28] H. D. Tsague and B. Twala, “First principle leakage current reduction technique for CMOS devices,” IEEE International Conference on Computing, Communication and Security (ICCCS), Pamplemousses, Mauritius, 4-5 December 2015.
[29] B. Zaidi, I. Saouane, C. Shekhar, “Simulation of Single-Diode Equivalent Model of Polycrystalline Silicon Solar Cells,” International Journal of Materials Science and Applications, Special Issue: Energy and Materials II. vol. 7, no. 1-1, pp. 8-10, 2018.
[30] T. M. Masiala, A. K. M. Bantu, G. E. Bakambo, J. M. Lunguya, J. L. K. Kanza, O. M. Muamba, “Influence of pH Preparation on the Photo-Response of Electrodeposited Titanium Dioxide (TiO2) Thin Films,” International Journal of Materials Science and Applications, vol. 5, no. 5, pp. 207-213, 2016.
Cite This Article
  • APA Style

    Muhammad Sana Ullah, Emadelden Fouad. (2018). Scrutiny of Leakage Currents with Insulating Materials for Transistor Applications. International Journal of Materials Science and Applications, 7(5), 167-173. https://doi.org/10.11648/j.ijmsa.20180705.11

    Copy | Download

    ACS Style

    Muhammad Sana Ullah; Emadelden Fouad. Scrutiny of Leakage Currents with Insulating Materials for Transistor Applications. Int. J. Mater. Sci. Appl. 2018, 7(5), 167-173. doi: 10.11648/j.ijmsa.20180705.11

    Copy | Download

    AMA Style

    Muhammad Sana Ullah, Emadelden Fouad. Scrutiny of Leakage Currents with Insulating Materials for Transistor Applications. Int J Mater Sci Appl. 2018;7(5):167-173. doi: 10.11648/j.ijmsa.20180705.11

    Copy | Download

  • @article{10.11648/j.ijmsa.20180705.11,
      author = {Muhammad Sana Ullah and Emadelden Fouad},
      title = {Scrutiny of Leakage Currents with Insulating Materials for Transistor Applications},
      journal = {International Journal of Materials Science and Applications},
      volume = {7},
      number = {5},
      pages = {167-173},
      doi = {10.11648/j.ijmsa.20180705.11},
      url = {https://doi.org/10.11648/j.ijmsa.20180705.11},
      eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ijmsa.20180705.11},
      abstract = {Continuous reducing the size of transistor technology has enabled extraordinary improvements in the switching speed, density, functionality and cost of microprocessors. Integrated Circuit industry is pursuing Moore’s curve down to deep-nanoscale dimensions. Advanced transistor technology now faces many challenges that together result in static power consumption due to leakage currents. In fact, leakage currents are responsible for more than 50% of the total power consumption in nanoscale designs. In deep-nanoscale arena, this percentage will increase further. However, diagnosing of the interface quality and interaction between insulators and semiconductors is significant to reduce the leakage current and achieve the high performance of switching devices in the nanoscale domain. Continuous scaling down has required drastic decreases of the SiO2 dielectric film thickness to achieve ever-higher capacitance densities. Fundamental limits of SiO2 as a dielectric material, imposed by electron tunneling, will be reached as this SiO2 film thickness approaches ~1nm. Therefore, alternate high-k interlayer dielectric material will be needed to replace SiO2 as a capacitor and gate dielectric material. Numerous alternate high-k materials are being actively investigated, ranging from Al2O3 (k ~ 9) to HfO2 (k ~ 25). High-k materials hold the promise of achieving very high capacitance densities with relatively thick films.},
     year = {2018}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - Scrutiny of Leakage Currents with Insulating Materials for Transistor Applications
    AU  - Muhammad Sana Ullah
    AU  - Emadelden Fouad
    Y1  - 2018/09/28
    PY  - 2018
    N1  - https://doi.org/10.11648/j.ijmsa.20180705.11
    DO  - 10.11648/j.ijmsa.20180705.11
    T2  - International Journal of Materials Science and Applications
    JF  - International Journal of Materials Science and Applications
    JO  - International Journal of Materials Science and Applications
    SP  - 167
    EP  - 173
    PB  - Science Publishing Group
    SN  - 2327-2643
    UR  - https://doi.org/10.11648/j.ijmsa.20180705.11
    AB  - Continuous reducing the size of transistor technology has enabled extraordinary improvements in the switching speed, density, functionality and cost of microprocessors. Integrated Circuit industry is pursuing Moore’s curve down to deep-nanoscale dimensions. Advanced transistor technology now faces many challenges that together result in static power consumption due to leakage currents. In fact, leakage currents are responsible for more than 50% of the total power consumption in nanoscale designs. In deep-nanoscale arena, this percentage will increase further. However, diagnosing of the interface quality and interaction between insulators and semiconductors is significant to reduce the leakage current and achieve the high performance of switching devices in the nanoscale domain. Continuous scaling down has required drastic decreases of the SiO2 dielectric film thickness to achieve ever-higher capacitance densities. Fundamental limits of SiO2 as a dielectric material, imposed by electron tunneling, will be reached as this SiO2 film thickness approaches ~1nm. Therefore, alternate high-k interlayer dielectric material will be needed to replace SiO2 as a capacitor and gate dielectric material. Numerous alternate high-k materials are being actively investigated, ranging from Al2O3 (k ~ 9) to HfO2 (k ~ 25). High-k materials hold the promise of achieving very high capacitance densities with relatively thick films.
    VL  - 7
    IS  - 5
    ER  - 

    Copy | Download

Author Information
  • Department of Electrical and Computer Engineering, Florida Polytechnic University, Lakeland, USA

  • Department of Natural Science, Florida Polytechnic University, Lakeland, USA

  • Sections